Get To Know The Physics Behind Soldering And The Packaging Of ICs

Often it feels as if soldering is deemed to be more of an art form than something that’s underpinned by the cold, hard reality of physics and chemistry. From organic chemistry with rosin, to the material properties of fragile gold bond wires and silicon dies inside IC packages and the effects of thermal stress on the different parts of an IC package, it’s a complicated topic that deserves a lot more attention than it usually gets.

A casual inquiry around one’s friends, acquaintances, colleagues and perfect strangers on the internet usually reveals the same pattern: people have picked up a soldering iron at some point, and either figured out what seemed to work through trial and error, or learned from someone else who has learned what seemed to work through trial and error. Can we say something scientific about soldering?

Defining the problems

The problems that affect the soldering of components – whether it involves soldering by hand or reflow/wave-soldering – essentially come down to oxidation, moisture ingress and temperature cycling. The first one is fairly obvious: copper oxidizes, which means that solder will not make a good connection. The second is mostly related to the (plastic) packaging of components as they absorb moisture and the issues this can cause.

The third and last problem is by far the most common thing which people argue about. Here the argument essentially concerns what constitutes a good solder joint. Often the use of a higher soldering temperature is listed as a good thing, as it supposedly shortens the soldering time per pad and with it the heating of the component, while also producing a better joint. In a moment we’ll see why that is not the case.

Moisture and soldering don’t mix

The moisture issue is something which one likely first encounters when ordering components from a store like Mouser or DigiKey and one receives the component in a bag that lists on the outside until what date the component can be soldered, along with a small card inside that has moisture-sensitive dyes on it to indicate whether moisture has entered the bag while it was in storage.

While at first this may seem strange, it begins to make sense when one realizes that the IC packaging isn’t water-proof, but that its molding compound will allow moisture through over time. While soldered into an active circuit, this isn’t a massive concern because it never gets hot enough to turn quickly into steam, but when soldering a component to the PCB, having moisture ingress can be fatal. The most extreme example of this is called ‘popcorning’. This concerns the heating up during soldering of moisture that has entered the molding component around the die.

As a result of this heating the moisture enters into a gaseous state, which massively increases its volume and consequently the pressure it exerts on the surrounding structures. This can crack the plastic molding, destroy features of the chip itself, break bond wires and so on. Essentially it will destroy the chip or damage it to the point where subsequent failure is unavoidable. A possible way to prevent damage from moisture ingress is by ‘baking’ the chip, gently heating the chip so that moisture is driven out of the chip packaging.

Soldering is an oxygen-free process

The main functions of solder flux are to remove existing oxidation, and to prevent new oxidation from forming.  To accomplish the former, most flux contains one or more chemicals which begin to decompose when exposed to the heat from the soldering process, resulting in the formation of acids that will react with any oxidation on the surface to be soldered. Flux intended to be used with electronics will use weak acids, whereas the type used for pipe fitting will have significantly more aggressive acids, often using zinc chloride or other chlorides, which produce hydrochloric acid. Most often electronic flux will be rosin flux, also called resin flux.

Defining rosin is hard, as there are many forms and classifications. Important to note there is that the rough classification involves the natural rosin that is extracted from pine trees, natural rosin that has been chemically modified to be more heat-resistant, and synthetic rosin, usually called ‘resin’.  Natural rosin is highly versatile, also finding uses in things like increasing the resistance of violin bow strings to make playing that instrument much easier.

Natural rosin flux is mildly active, but can be made stronger by adding different activator chemicals.  This means that any type of rosin flux will have different properties, including a different activation and maximum temperature.

With the surface to be soldered on cleaned of oxidation, the acid has done its job. Next is to ensure that the surface doesn’t reoxidize while the component is being soldered down. This is done with chemicals whose task is to provide an oxygen barrier so that oxidation becomes impossible. Generally this is also the task of the rosin or equivalent substance. This means that the protective effect lasts for as long as this barrier is present. This property leads to the issue of soldering temperature.

Temperature: when more isn’t better

Because the conversion of rosin to acid depends on thermal activation, acid will be produced faster when the soldering temperature is increased. But this also means that the rosin gets used up faster and the oxygen barrier vanishes sooner. Higher temperatures also increase the oxidation rate, so there’s an optimal soldering window that is determined by both the amount of starting flux and the soldering temperature.

If we look at a common lead-based solder such as 245 CORE Sn63Pb37 from Kester, we can see from its Material Safety Data Sheet (MSDS)  using the CAS number given for the rosin core (#65997-06-0) that it uses a modified rosin type from Eastman Chemical Company, called Staybelite Resin-E Partially Hydrogenated Resin. Its datasheet lists its properties as having a melting point between 55.2 °C and 72.1 °C, and a boiling point of 265 °C.

The recommended hand soldering temperature according to ESA (ECSS-Q-ST-70-08, section 5.6.7) is about 280-350 °C (up to 320 °C in the older PSS-01-708 standard), which in the case of the above lead-based solder means that the rosin flux will begin to activate first, at 55 °C, followed by the melting of the lead at about 184 °C (191 °C for 60/40 leaded). This gives about a 100-170 °C thermal window.

From left to right: Sn-Ag-Cu, Sn-Cu-Ni and Sn-Pb, all at 300 °C.

Research by Fraunhofer ISIT engineer Thomas Ahrens (link to PDF in German) examines what happens during various hand soldering temperatures. This research shows how higher soldering tip temperatures (300-375 °C) strongly reduces the time before PCB damage (‘measling’) occurs. It also shows for through-hole components that 300 °C produces excellent results, whereas the lead-free solders used (Sn-Ag-Cu, Sn-Cu-Ni) need a bit higher temperature to flow properly onto THT headers.

Don’t cycle that temperature

Along with the issue of moisture ingress – as covered earlier – IC packages are quite fragile structures, as is detailed exquisitely by Dr. Shirley at Portland State University in his presentation titled ‘Plastic Package Reliability‘. In addition to the moisture related issues, this document also covers heat-stress. Much of this is caused by thermal cycling during assembly, which can take a wide variety of shapes.

The effect of temperature cycling can cause new defects (e.g. cracks) in the molding compound, the die, bond wires and so on. It can also cause new cracks to be formed. This is why the ESA soldering standard referenced earlier requires that one attaches small heatsinks to the leads of any thermally sensitive devices. The effects of thermal cycling can be as disastrous as mechanical shearing literally destroying bond wires.

One may remember that in the datasheets for ICs one can usually find recommended and maximum soldering temperatures. These indicate just how warm the package can become before damage becomes inevitable. Since reality isn’t perfect, it’s a good idea to stay far below these indicated numbers in so far as possible. Even when damage isn’t immediately apparent, the action of over-heating part of an IC as well as heating it up and then cooling it down too quickly may have caused damage that may mean that the part will fail in a matter of weeks or months after assembly.

Putting it all together

The important message when it comes to soldering and doing it properly is that it’s all about the science behind it. At institutions like NASA, ESA, and those who make equipment for them, failure literally isn’t an option, which is why they have spent so much effort on understanding these failure modes and how to prevent them. Meanwhile manufacturers of solder and fluxes have many decades of knowledge and experience.

What is the price of doing things wrong? In hobby use, you can get away with pretty bad things when it comes to soldering. Chips won’t instantly die when soldered at 450 °C for two seconds without preheating, but one may have caused small fractures that will slowly destroy the chip during thermal cycles. If you use the gadget indoors for only a few years, you might never notice.

The important thing to know is what is needed to get that proper solder joint and not exceed it. When the science shows that soldering lead-based at 300 °C works, then there’s no point in soldering at 375 °C. If anything, one risks poor joints by cooking off the rosin flux and getting oxidation on the pad before solder can bond with it.

Finally, with NASA’s soldering practices they have had Spirit and Opportunity as well as many other Mars rovers and satellites perform flawlessly for years. Not to mention Voyager 1 and 2, traveling into interstellar space since they were launched in 1977. If those aren’t perfect solder joints, then I don’t know what are.

22 thoughts on “Get To Know The Physics Behind Soldering And The Packaging Of ICs

  1. I myself tend to aim at keeping solder temperatures fairly low. Usually around the 250-300 C area.

    Though, the problem of rosin boiling away can be fixed by adding an excess of rosin to start with. (after all, one should generally clean it off after anyway.)

    But it is never fun to see a board delaminate itself under high temperatures. (Though, this varies with board material, some is better then others. Phenolic paper boards tends to delaminate and discolor just seeing an iron in my experience… Unlike FR4 that usually doesn’t care even when abused.)

    1. FR4 doesn’t much care about reasonable or slightly unreasonable temps, but the bond for the surface copper generally does. Keeping the temp reasonable and the time short reduces the risk.

    2. FR4 loses most of its strength above its glass transition temperature (around 130C). If there’s any stress on a component or a pad (like a heavy hand on the iron), it’s easy to tear away from the board at that temp (before the solder is even melted). It doesn’t take much force to even delaminate FR4 when it’s hot. Approximately nobody is in the habit of grabbing hot boards and flexing them, but try it some time: it’s surprising how weak they become.

      1. It’s also easy to warp an FR4 PCB that way — support it in alligator clips that aren’t quite coplanar and heat it up past Tg. The softened board readily bends under the torque of the misaligned clips, and cooling below Tg sets the bend semi-permanently. Makes sliding the board back into the linear guides in its enclosure all sorts of fun until you realize what you were doing wrong.

  2. thanks for the superb educational article, soldering for years and getting away with it, self taught pre-internet etc as the opening bit says, so always good to learn stuff

    1. Just been soldering up a project and turned my 936D clone down to 360.
      Didn’t quite hack it so went up to 380 and found a sweet spot

      I’ll admit I’m sitting 20-30deg below normal and just being more patient.
      It’s not as fast but maybe it’s of benefit.

      I tend to de-solder on it around 420 – 430 which works well for me with old pres button vac tube I’ve used for a looooong time

      1. It would interesting to get an accurate measurement of tip temperature you might find your actual temps are much lower than the displayed temp.

        I know my no name station from Jaycar reads 257deg but tip temp is varies between 308 and 340 deg.

        When I first started using it When set around 300 it was obvious the joints were too hot. So like you I kept adjusting the temp to get a nice joint – just measured it now and the measured figures match the experience.

    1. Interesting point… I just had to dig into that now :) As it turns out, industrial temperature range has a lower limit of -40°C, military being -55°C and a spectrometer on Voyager 1 is now down to -79°C (dry ice in earth standard conditions).
      Besides the infant mortality that would be a pain with satellites, deep cooling will also be hard on electronics, no idea what the long-term effects of that static scenario are though.

      https://www.nasa.gov/mission_pages/voyager/voyager20120117.html

      On another note and for what it’s worth: I killed two SO-8 opamps by cycling them between -268°C and room temperature three or four times… epoxy moulded parts are really bad at deep temperature cycling.

    1. Sockets! I remember those! I still have a few, stored with my wirewrapping tools… Wirewrapping would also be a great way way to avoid thermal shock.

      Have you noticed how few chips are even available in DIP any more? (At least among the ones designed in this millennium.)

  3. Copper oxidizes, but solder does as well, particularly when heated…

    One of my “tricks” is to always add fresh solder to an iron’s tip before setting it back in a holder, and always wiping off solder (I prefer a sponge) from the tip when removing the iron from the holder. I have the same wide wedge tip on a 25w iron I’ve been using for over 20 years (!!!). I have temp controlled irons and hot air reflow, but that old iron still gets the most use.

    My nutshell soldering recommendations (in addition to above):

    Practice on junk – old burnt boards, etc. See what it takes to lift traces off different boards, how heat travels, how a fresh blob of rosin core solder compares to heat only, etc. An instructor once had us solder up stripped clean solid core wires in a grid, which was a good exercise to go through.

    Clean is clean only briefly, solder quickly after exposing metal to air. Don’t bother trying to solder when contaminants are present – oil from fingers, etc.

    Mass is key to soldering – a more massive tip holds more heat, and more readily transfers that heat to another surface. A 500c pencil tip won’t work on, ex, 8 awg wire. Time and temperature AND MASS are all intertwined. A heavier, larger tip will also allow for faster work across multiple connections. Meanwhile, for sensitive devices, a smaller tip will allow focused heat at a pinpoint location, as long as time is kept to a minimum – more time, more thermal transfer, more device heating and thermal stress. A huge tip isn’t the perfect answer, but understanding how different tips work will help you choose the right tool for the job and gain a better feel for soldering in general, IMO.

    When tinning wires (which I do for any soldered wire), I start by applying heat at the insulation side of a stripped piece of wire and chase the heat to the end of the wire quickly once the solder starts to flow into the wire. I will apply solder to keep it wet, and try to keep a bead of solder to saturate the wire – it’s plenty clean to snip the end of the wire to remove a remaining solder blob or tag, versus having a mess by the insulation side.

    I use warm to hot water on a sponge (not fond of any other tip cleaners I’ve tried), and wring the sponge to damp and not dripping so as not to pull too much heat from the iron when cleaning – let steam do the work.

    If I see a spot oxidizing on a tip, I’ll go after it with fresh rosin core solder. I always use rosin core on wiring. I use organic core from time to time (water soluble), but I find it pickier about cleanliness than rosin core.

    I’m a fan of leaded solder, and have done reflow at home w/ Kester lead based solder (no clean up flux), with great results.

    One last – solder is generally quite heavy, and a wet tip and some gravity can be extremely effective at removing excess solder. Never found a lot of value in mechanical spring loaded solder suckers, but I used to LOVE an old Pace through hole desoldering station I’d rejuvenated. Otherwise, fresh (new, non-oxidized) wick w/ rosin dust in it is my favorite.

    Experience? I used to build and repair boards – through hole and surface mount – as a job (thousands of boards). I build my own boards at home from time to time, and I don’t hesitate to repair my own gear or fix something for a friend. Even at my current job (not electronics), I find occasions to break out an iron – it’s a skill I can’t imagine quitting.

  4. I’m really curious about the new Metcal / OKI CV-500 soldering station. It seems to be smart enough to judge intermetallic bonding between the solder and pads while you are soldering, basically taking out a lot of guesswork out of the hand soldering process.
    I’d really like to try and see how it is to work with that station.
    Aside from that, nice, interesting article. Keep them coming!

  5. Regular cleaning with a very quick wipe on a just moist sponge to take off any trace of old solder on the tip that has oxidised before beginning the next join is essential.

    In my teaching days it was hard work to get students to understand solder is not glue, and is not carried on the soldering iron tip to be “pasted” on the join ( while the resin disappears as smoke). Cold joints were rife on student projects, but wrecked PCBs surprisingly rare. Students who wrecked tips by melting plastic (acidic!t!) got serious detentions.

    I likened each join to a miniature chemical reaction they had to get right, rather than just a physical process of holding components to the board.

  6. Very Interesting, both the article and some comments. I try to learn something new every day. This is one of those days. I learned to solder from my dad and have been at it over 50 years. Never done some of the methods described, only straight forward stuff. A good solider connection is achieved every time if you clean the material, mechanically connect whenever possible, proper size iron, use rosin sparingly, place tip near bottom so heat rises and touch solder to connection near top and watch solder flow through out and down toward iron tip. Works every time. Don’t over complicate.

Leave a Reply to HalencoCancel reply

Please be kind and respectful to help make the comments section excellent. (Comment Policy)

This site uses Akismet to reduce spam. Learn how your comment data is processed.